Título: | Composition-, temperature- and pressure-induced transitions between high-pressure stabilized perovskite phases of the (1-x)BiFe0.5Sc0.5O3 - xLaFe0.5Sc0.5O3 series |
Autor: | Salak, A.N. Cardoso, J.P. Khalyavin, D.D. Barbier, A. Fertey, P. Mikhalev, S.M. Olekhnovich, N.M. Pushkarev, A.V. Radyush, Yu V. Stanulis, A. Ramanauskas, R. |
Palavras-chave: | High-pressure synthesis Metastable perovskite phase Incommensurate modulation |
Data: | 25-Fev-2023 |
Editora: | Elsevier |
Resumo: | Crystal structures of the high-pressure synthesized perovskite phases of the (1-x)BiFe0.5Sc0.5O3-xLaFe0.5Sc0.5O3 (0 = x ≤ 1) system and their temperature and pressure behaviours were studied using laboratory and synchrotron X-ray diffractions as well as neutron diffraction. At room temperature, the as-prepared phases with x ≤ 0.05 have an antipolar structure with the Pnma symmetry and with the √2ap × 4ap × 2√2ap superstructure (where ap is the pseudocubic perovskite unit-cell parameter). An incommensurately modulated phase with the Imma(00γ)s00 superspace group is observed for 0.10 = x ≤ 0.33, while a non-polar Pnma phase (√2ap × 2ap × √2ap) is stable when x ≥ 0.34. The antipolar Pnma phase in the as-prepared samples with composition corresponding to x = 0 transforms into the polar Ima2 one via irreversible annealing-caused transformation accompanied by a formation of a high-temperature intermediate polar R3c polymorph, while the antipolar Pnma phase in samples with x = 0.05 is stable until the decomposition temperature. In the solid solutions with 0.10 = x ≤ 0.33, increasing temperature was found to result in a reversible transformation of the Imma(00γ)s00 phase into a non-polar Pnma one. The transition temperature decreases with increasing x. A hydrostatic pressure of few GPa was also shown to induce a reversible Imma(00γ)s00 → Pnma transformation. |
Peer review: | yes |
URI: | http://hdl.handle.net/10773/36540 |
DOI: | 10.1016/j.jssc.2023.123937 |
ISSN: | 0022-4596 |
Aparece nas coleções: | CICECO - Artigos |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
jssc322_123937.pdf | 1.1 MB | Adobe PDF | Ver/Abrir |
Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.