Title: | Estudo de propriedades elétricas e estruturais de BiNbO4 |
Author: | Ferreira, Carina Sofia Vaz Ramos Alves |
Advisor: | Graça, Manuel Costa, Luís Cadillon |
Keywords: | Engenharia física Niobato de bismuto - Propriedades eléctricas Espectroscopia de impedância Dieléctricos Cerâmica electrónica |
Defense Date: | 2014 |
Publisher: | Universidade de Aveiro |
Abstract: | Este trabalho teve como objetivos preparar niobato de bismuto (BiNbO4) na forma de material cerâmico e estudar as propriedades elétricas relacionando-as com a microestrutura e morfologia. A influência do método de preparação nas propriedades foi um dos parâmetros de análise.
Foram preparados pós de BiNbO4 por reação de estado sólido e por sol-gel. Pastilhas destes pós foram submetidas a tratamentos térmicos a diferentes temperaturas, com base nos resultados obtidos por análise térmica do pó base. As amostras foram estudadas a nível estrutural através de difração de raios-X (DRX) e espetroscopia de Raman. Morfologicamente o estudo efetuou-se através de microscopia eletrónica de varrimento (MEV). As características elétricas destas amostras foram analisadas em função da temperatura (200 K a 400 K) e em função da frequência (100 Hz a 5 GHz). A medição da condutividade dc entre 200 e 400 K também foi realizada. The main objective of this work was to prepare bismuth niobate (BiNbO4) in the form of ceramic material and study its electrical properties regarding microstructure and morphology. The influence of the preparation method on the properties was also a focus on this analysis. The BiNbO4 powders were prepared by solid state reaction and sol-gel. Pellets of the powders were submitted to thermal treatments at different temperatures, based on the results obtained by thermal analysis of the base powder. The samples were studied at structural level through X-Ray diffraction and Raman spectroscopy. Regarding morphology, the study was made by scanning electron microscopy (SEM). The electric characteristics of the samples were studied in terms of temperature (200 K to 400 K) and in terms of frequency (100 Hz to 5 GHz). DC conductivity between 200 and 400 K was also done. |
Description: | Mestrado em Engenharia Física |
URI: | http://hdl.handle.net/10773/14275 |
Appears in Collections: | UA - Dissertações de mestrado DFis - Dissertações de mestrado |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
Estudo de propriedades elétricas e estruturais de BiNbO4.pdf | 4.49 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.