Title: Perovskite-like LaNiO3-δ as oxygen electrode material for solid oxide electrolysis cells
Author: Yaremchenko, Aleksey
Arias-Serrano, Blanca I.
Zakharchuk, Kiryl
Frade, Jorge R.
Issue Date: 2019
Publisher: Electrochemical Society
Abstract: Perovskite-like LaNiO3-δ was evaluated as potential oxygen electrode material for solid oxide electrolysis cells. Compared to the Ruddlesden-Popper Lan+1NinO3n+1 (n = 1,2,3) counterparts, LaNiO3-δ exhibits higher p-type metallic-like conductivity under oxidizing conditions (450 S×cm-1 at 800°C for highly porous ceramics) together with a moderate thermal expansion coefficient (13.7 ppm×K-1 in air at 25-800°C) compatible with common solid electrolytes. The measured electrode polarization resistance (Rη) in contact with YSZ, CGO and LSGM solid electrolytes was 1.4, 0.77 and 0.22 Ω×cm2 at 800°C, and 208, 123 and 7.1 Ω×cm2 at 600°C, respectively, under zero-current conditions in air. Surface modification of via PrOx infiltration resulted in lower values of Rη (0.024 Ω×cm2 at 800°C and 0.76 Ω×cm2 at 600°C) and low anodic overpotentials (20 mV at 800°C and 500 mA×cm-2) in contact with LSGM.
Peer review: yes
DOI: 10.1149/09101.2399ecst
ISSN: 1938-5862
Appears in Collections:CICECO - Artigos
DEMaC - Artigos

Files in This Item:
File Description SizeFormat 
ECSTrans_91_(2019)_2399.pdf576.01 kBAdobe PDFView/Open

Formato BibTex MendeleyEndnote Degois 

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.