 Fabrication of solar cells from poly(3-hexylthiophene) and ZnO Nanostructures
Please use this identifier to cite or link to this item http://hdl.handle.net/10773/2289

title: Fabrication of solar cells from poly(3-hexylthiophene) and ZnO Nanostructures
authors: Gonfa, Belete Atomsa
advisors: Barros, Ana
Cunha, António Ferreira da
keywords: Ciência dos materiais
Nanomateriais
Células fotovoltaicas
Óxido de zinco
issue date: 2009
publisher: Universidade de Aveiro
abstract: As células fotovoltaicas à base de compostos orgânicos e de híbridos do tipo orgânico/inorgânico têm recebido bastante atenção devido à sua potencial aplicação como fonte de energia limpa e económica. A utilização de nanoestruturas neste tipo de dispositivos tem também recebido especial atenção já que o confinamento quântico a elas associado promove a percolação, facilitando a passagem dos portadores de carga o que aumenta a sua eficiência. Nesta tese foram preparados dispositivos fotovoltaicos “bulk heterojunction” através da mistura de poli(3-hexiltiofeno) com diferentes nanoestruturas de ZnO. As nanoestruturas de ZnO (nanopartículas, nanofios e naofibras) foram preparadas por diferentes técnicas e caracterizadas por XRD, espectroscopia no UV-Vis, SEM e TEM. As nanopartículas e os nanofios de ZnO foram preparadas por métodos químicos em solução e decomposição térmica de acetato de zinco dihidratado respectivamente. As naonofibras de ZnO foram preparadas por calcinação de nanofibras compostas por alcóol polivinílico e acetato de zinco preparadas por “electrospinning”. As nanoestruturas preparadas foram ainda funcionalizadas com o ácido pireno-1-carboxílico. As nanoestruturas preparadas, funcionalizadas ou não funcionalizadas, foram misturadas com soluções de P3HT de modo a preparar dispositivos fotovoltáticos em duas configurações distintas. Numa delas os eléctrodos consistem em ITO e o alumínio depositado por evaporação térmica, na outra, os eléctrodos consistem em ITO e tinta de prata. O primeiro tipo de configuração utilizou a seguinte sequência: vidro/ITO/PEDOT:PSS/camada fotoactiva/Al. Na segunda configuração a sequência utilizada foi: vidro/ITO/ZnO/ camada fotoactiva/ PEDOT:PSS/Ag. As camadas de PEDOT:PSS bem como as camadas fotoactivas foram depositadas por spin coating. A caracterização dos dispositivos foi feita através de medições da corrente-tensão sob condições simuladas de iluminação padrão. Os dispositivos preparados apresentaram actividade fotovoltaica mas a sua eficiência ainda precisa de ser melhorada. ABSTRACT: Organic and organic/inorganic hybrid solar cells have been receiving a significant amount of attention due to their potential to yield environmentally friendly and cheap source of energy. As a result they are being investigated widely. Making use of nanostructures in such devices has also received a great attention as they provide percolative pathways for charge carriers by quantum confinement, helping in the improvement of the efficiency of the devices. In this thesis bulk heterojunction photovoltaic devices have been produced by blending different ZnO nanostructures and surface functionalized ZnO nanostructures with poly- 3-hexylthiophene. ZnO nanostructures (nanoparticles, nanowires and nanofibers) have been produced by different techniques and characterized by XRD, UV-Visible spectroscopy and SEM. ZnO nanoparticles and ZnO nanowires were prepared by wet chemical synthesis and thermal decomposition of zinc acetate dihydrate respectively. ZnO nanofibers were prepared by calcination of polyvinyl alcohol/zinc acetate composite nanofiber, which had been produced by the electrospinning process. These nanostructures were also surface functionalized with pyrene-1-carboxylic acid and characterized. Subsequently, these nanostructures and their surface functionalized forms were used to fabricate photovoltaic devices by combining them with P3HT and its whiskers. The photovoltaic devices have been prepared in two different configurations. In some ITO and aluminium deposited by thermal evaporation were used as the electrodes, while in the others ITO and silver paste were used. The first set of devices had the order glass/ITO/PEDOT:PSS/photoactive layer/Al, while the latter had the order lass/ITO/ZnO/photoactive layer/ PEDOT:PSS/Ag paste. The PEDOT:PSS and the photoactive layers were deposited by spin coating of the suspension of PEDOT:PSS in water and the suspension of the ZnO nanostructures in the poly-3-hexylthiophene solution respectively. The photovoltaic cells were finally characterized by current-voltage characteristics measurement under simulated standard illumination conditions. The photovoltaic devices prepared have demonstrated photovoltaic properties, but their efficiencies need further improvement.
description: Mestrado em Ciência dos Materiais
URI: http://hdl.handle.net/10773/2289
appears in collectionsCV - Dissertações de mestrado
UA - Dissertações de mestrado

files in this item

file sizeformat
2009001118.pdf4.21 MBAdobe PDFview/open
statistics

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

 

Valid XHTML 1.0! RCAAP OpenAIRE DeGóis
ria-repositorio@ua.pt - Copyright ©   Universidade de Aveiro - RIA Statistics - Powered by MIT's DSpace software, Version 1.6.2