dc.contributor.advisorFernandes, Hugo Alexandre Gonçalves da Rochapt_PT
dc.contributor.advisorMantas, Pedropt_PT
dc.contributor.advisorDuarte, João Miguel Baratapt_PT
dc.contributor.authorSilva, Paulo Netopt_PT
dc.date.accessioned2023-12-11T11:04:59Z-
dc.date.issued2023-11-20-
dc.identifier.urihttp://hdl.handle.net/10773/39782-
dc.description.abstractEste relatório descreve o trabalho realizado no estágio desenvolvido na unidade industrial da Torrecid Portugal Lda, produtores de vidrados cerâmicos. O problema proposto está relacionado com o aumento das importações e com o aumento dos preços energéticos e de custos de produção de produtos cerâmicos. Sendo assim, o objetivo do estágio foi criar efeitos inovadores em vidrados cerâmicos em diferentes tipos de vidrados (brilho transparente e reativo de cristais de rútilo) e em diferentes suportes cerâmicos (monoporosa e em louça de grés), com a utilização de matérias-primas pouco utilizadas na indústria cerâmica, tais como, sesquióxido de bismuto, sesquióxido de antimónio, trióxido de tungsténio e bórax penta-hidratado. Realizou-se a formulação dos dois tipos de vidrados e posteriormente, a formulação desses vidrados com a adição de concentrações de 2%, 5% e 10% das matérias-primas em estudo. Consoante o interesse nos efeitos visuais gerados pelas matérias-primas, formularam-se novas concentrações de modo a compreender melhor os efeitos visuais criados. Foram realizados ensaios de colorimetria, dilatometria, resistência química e à mancha, teste de fluidez em fundido, espetroscopia dispersiva de raios X (EDS), difração de raios X (DRX), microscopia eletrónica de varrimento (MEV) e análises térmicas, de modo a explicar os efeitos visuais obtidos. Foi verificado experimentalmente que o sesquióxido de antimónio e o trióxido de tungsténio conferem brancura aos vidrados de brilhos transparentes e que criam efeitos inovadores no vidrado reativo de cristais de rútilo. No caso do bórax penta-hidratado e do óxido de bismuto foi observado um aumento na transparência nos vidrados de brilhos transparentes e uma dissipação do efeito reativo nos vidrados reativos de cristais de rútilo.pt_PT
dc.description.abstractThis report describes the work carried out in the internship developed in the industrial unit of Torrecid Portugal Lda, producers of ceramic glaze. The proposed problem relates to the increase in imports of ceramic products in recent years. This problem is related to rising energy prices and production costs. Thus, the objective of the internship was to create innovative effects in ceramic glazing in different types of glazing (transparent and reactive gloss of rutile crystals) and in different ceramic supports (monoporous and in dishware stoneware), with the use of raw materials little used in the ceramic industry, such as, bismuth sesquioxide, antimony sesquioxide, tungsten trioxide and borax pentahydrate. The formulation of the two types of glazed was carried out, and later, the formulation of these glazed with the addition of concentrations of 2%, 5% and 10% of the raw materials under study. Depending on the interest in the visual effects generated by the raw materials, new concentrations were formulated to better understand the visual effects created. After obtaining the samples, colorimetry tests were performed by the CIELab method, to obtain a numerical value of the colour parameters of the visual effects and to be able to make a direct comparison between the samples with raw materials and the standard glazes. Also dilatometry, chemical resistance, melt flow test, X-ray dispersive spectroscopy (EDS), XRD, scanning electron microscopy (SEM) and thermal analysis were performed in order to explain the visual effects obtained. It has been experimentally verified that antimony sesquioxide and tungsten trioxide impart whiteness to transparent glossy glazes and that they create innovative effects in the reactive glaze of rutile crystals. In the case of hydrated penta borax and bismuth oxide, an increase in transparency was observed in transparent gloss glazes and a dissipation of the reactive effect in rutile crystal reactive glazes.pt_PT
dc.language.isoporpt_PT
dc.rightsembargoedAccesspt_PT
dc.rights.urihttps://creativecommons.org/licenses/by/4.0/pt_PT
dc.subjectVidradospt_PT
dc.subjectFritaspt_PT
dc.subjectGréspt_PT
dc.subjectMonoporosapt_PT
dc.subjectBrilho transparentept_PT
dc.subjectReativospt_PT
dc.subjectSesquióxido de antimóniopt_PT
dc.subjectTrióxido de tungsténiopt_PT
dc.subjectÓxido de bismutopt_PT
dc.subjectBórax penta-hidratadopt_PT
dc.titleEstudo da influência de novos materiais na formulação de vidrados cerâmicospt_PT
dc.typemasterThesispt_PT
thesis.degree.grantorUniversidade de Aveiropt_PT
dc.date.embargo2028-11-20-
dc.description.masterMestrado em Engenharia de Materiaispt_PT
Appears in Collections:UA - Dissertações de mestrado
DEMaC - Dissertações de mestrado

Files in This Item:
File Description SizeFormat 
Documento_Paulo_Silva.pdf5.52 MBAdobe PDFembargoedAccess


FacebookTwitterLinkedIn
Formato BibTex MendeleyEndnote Degois 

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.