dc.description.abstractEsta dissertação, consiste num trabalho desenvolvido no âmbito do estágio de mestrado em ambiente empresarial nas instalações da CIRES, tendo como objetivo desenvolver um polímero reticulado, termicamente estável a fim de melhorar as propriedades finais do poli(cloreto de vinilo). Este polímero, pode ser utilizado em diversas aplicações finais contudo, apresenta algumas limitações a nível da estabilidade térmica. Assim, com vista a melhorar as propriedades do PVC, foi adotada uma técnica de reticulação por via química utilizando um copolímero de cloreto de vinilo de base silano. Numa primeira etapa, procedeu-se à pesquisa bibliográfica e selecionou-se a metodologia de reticulação a seguir, bem como a natureza do silano e aditivos. O silano utilizado foi o 3-metacril-oxipropil-trimetoxissilano (A174), e variou-se a sua concentração no copolímero de base PVC. Na etapa de composição e processamento foram testados alguns aditivos e diferentes condições operatórias com o intuito de reduzir a ocorrência de reticulação nesta fase. De seguida as amostras foram sujeitas a reações de hidrólise e condensação, denominada de etapa de cura, durante a qual ocorre reticulação para deste modo obter um PVC reticulado. Nesta etapa foi utilizado um catalisador de base estanho, nomeadamente o dilaurato de dioctilestanho (DOTL) de forma a potenciar a reação de condensação. Os produtos obtidos foram analisados relativamente ao teor de insolúveis através da extração soxhlet, o que permitiu selecionar as melhores amostras, isto é, as que apresentavam um grau de reticulação mais elevado. Depois de escolhidas as amostras com melhores resultados, foram efetuadas análises para avaliar o seu desempenho térmico por TGA, termomecânico por DMA e ainda mecânico através de testes de tração. Concluiu-se assim que comparativamente às amostras de referência, as amostras reticuladas apresentaram melhorias significativas.pt_PT
dc.description.abstractThis dissertation was developed within the scope of an internship carried out in an industrial environment at CIRES’s headquarters. The main objective was development of a thermally stable crosslinked polymer in order to enhance the final properties of the poly(vinyl chloride) (PVC). This polymer can be utilized in many end use applications, however, it presents a few limitations regarding its thermal stability. Thus, in order to improve the properties of PVC, a chemical crosslinking route was adopted using a silane-based vinyl chloride copolymer. Initially, a bibliographic review was carried out and the crosslinking methodology was selected, as well as the type of silane and additives to be used. The silane that was utilized was the 3- methacryl-oxypropyl-trimetoxysilane (A174), and its concentration was varied in the PVC-based copolymer. During the composition and processing stage, additives and operating conditions were tested with the intent of reducing the occurrence of crosslinking at this stage. Afterwards, the samples were submitted to hydrolysis and condensation reactions, referred to as curing, during which crosslinking takes place to afford crosslinked PVC. A tin-based catalyst, specifically dioctylin dilaurate (DOTL), was used to enhance the condensation reaction. The content of insoluble materials of the products was determined using the soxhlet extraction and the best samples were chosen, i.e. those that presented the highest crosslinking level. Having selected the samples whose results were the most promising, there were submitted to different analyses in order to evaluate their thermal performance by TGA, the thermomechanical performance by DMA, and also the mechanical performance using stress-strain tests. It can be concluded that, in comparison with the reference samples, the crosslinked samples showed significant improvements.pt_PT
dc.language.isoporpt_PT
dc.rightsembargoedAccesspt_PT
dc.rights.urihttps://creativecommons.org/licenses/by/4.0/pt_PT
dc.subjectPoli(cloreto de vinilo)pt_PT
dc.subjectCloreto de vinilopt_PT
dc.subjectReticulaçãopt_PT
dc.subjectSilanospt_PT
dc.titleMelhoria das propriedades mecânicas do poli(cloreto de vinilo)pt_PT
dc.typemasterThesispt_PT
thesis.degree.grantorUniversidade de Aveiropt_PT
dc.date.embargo2027-12-30-
dc.description.masterMestrado em Engenharia Químicapt_PT
Appears in Collections:UA - Dissertações de mestrado
DQ - Dissertações de mestrado

Files in This Item:
File Description SizeFormat 
Documento_Soraia_Pinto.pdf5.04 MBAdobe PDFembargoedAccess


FacebookTwitterLinkedIn
Formato BibTex MendeleyEndnote Degois 

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.