Please use this identifier to cite or link to this item: http://hdl.handle.net/10773/20491
Full metadata record
DC FieldValueLanguage
dc.contributor.authorMota, D. A.pt
dc.contributor.authorRomaguera-Barcelay, Y.pt
dc.contributor.authorTkach, A.pt
dc.contributor.authorPerez de la Cruz, J.pt
dc.contributor.authorVilarinho, P. M.pt
dc.contributor.authorTavares, P. B.pt
dc.contributor.authorAgostinho Moreira, J.pt
dc.contributor.authorAlmeida, A.pt
dc.date.accessioned2017-12-07T19:48:55Z-
dc.date.available2017-12-07T19:48:55Z-
dc.date.issued2013pt
dc.identifier.issn0021-8979pt
dc.identifier.urihttp://hdl.handle.net/10773/20491-
dc.description.abstractDeliberately oxygen deficient potassium tantalate thin films were grown by RF magnetron sputtering on Si/SiO2/Ti/Pt substrates. Once they were structurally characterized, the effect of oxygen vacancies on their electric properties was addressed by measuring leakage currents, dielectric constant, electric polarization, and thermally stimulated depolarization currents. By using K2O rich KTaO3 targets and specific deposition conditions, KTaO3-delta oxygen deficient thin films with a K/Ta = 1 ratio were obtained. Room temperature X-ray diffraction patterns show that KTaO3-delta thin films are under a compressive strain of 2.3% relative to KTaO3 crystals. Leakage current results reveal the presence of a conductive mechanism, following the Poole-Frenkel formalism. Furthermore, dielectric, polarization, and depolarization current measurements yield the existence of a polarized state below T-pol similar to 367 degrees C. A Cole-Cole dipolar relaxation was also ascertained apparently due to oxygen vacancies induced dipoles. After thermal annealing the films in an oxygen atmosphere at a temperature above T-pol, the aforementioned polarized state is suppressed, associated with a drastic oxygen vacancies reduction emerging from annealing process. (C) 2013 AIP Publishing LLC.pt
dc.language.isoengpt
dc.publisherAMER INST PHYSICSpt
dc.relationinfo:eu-repo/grantAgreement/FCT/5876-PPCDTI/64805/PTpt
dc.relationinfo:eu-repo/grantAgreement/FCT/SFRH/SFRH%2FBPD%2F34607%2F2007/PTpt
dc.relationinfo:eu-repo/grantAgreement/FCT/COMPETE/132936/PTpt
dc.rightsopenAccesspor
dc.subjectSTRONTIUM-TITANATEpt
dc.subjectSRTIO3pt
dc.subjectFERROELECTRICITYpt
dc.subjectPEROVSKITESpt
dc.subjectDISPERSIONpt
dc.subjectTANTALATEpt
dc.subjectDEFECTSpt
dc.subjectOXIDEpt
dc.titleInduced polarized state in intentionally grown oxygen deficient KTaO3 thin filmspt
dc.typearticlept
dc.peerreviewedyespt
ua.distributioninternationalpt
degois.publication.issue3pt
degois.publication.titleJOURNAL OF APPLIED PHYSICSpt
degois.publication.volume114pt
dc.relation.publisherversion10.1063/1.4813324pt
dc.identifier.doi10.1063/1.4813324pt
Appears in Collections:CICECO - Artigos



FacebookTwitterLinkedIn
Formato BibTex MendeleyEndnote Degois 

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.