Please use this identifier to cite or link to this item: http://hdl.handle.net/10773/11158
Title: Argamassas de colagem para superfícies de aderência difícil
Author: Pinho, Cátia Vanessa de Oliveira
Advisor: Ferreira, Víctor Miguel Carneiro de Sousa
Silva, Luís Miguel Cardoso da
Keywords: Engenharia civil
Argamassas
Revestimentos cerâmicos - Aderência
Defense Date: 2012
Publisher: Universidade de Aveiro
Abstract: No presente trabalho, foram caracterizados diversos tipos de argamassas-cola para aderência de superfícies difíceis. Esta caracterização foi realizada em argamassas em pó, no estado fresco e após endurecimento, de modo a determinar a mais adequada para os objetivos propostos. Posteriormente, foi caracterizada a lâmina cerâmica, com e sem rede no tardoz. Esta caracterização foi realizada tendo em atenção a absorção de água, porosidade aberta, permeabilidade ao vapor de água, perda de massa por calcinação a 500º e 900ºC e avaliação da aderência utilizando a seleção de argamassas realizada anteriormente. Face às diferenças de resultados obtidos nos testes de aderência da lâmina, com e sem rede no tardoz, optou-se pela reconstrução do tardoz da lâmina cerâmica. Esta reconstrução foi realizada variando o tipo de rede, o tipo de cola de fixação e o tipo de agregados colados de modo a melhorar a aderência, sendo posteriormente estudada a aderência com estas novas superfícies. Não tendo sido atingidos os resultados expectáveis, decidiu-se avaliar o processo de secagem e o efeito do pente utilizado na aplicação da argamassa, uma vez que este último influencia na quantidade de argamassa envolvida no processo. Foi ainda avaliada a compatibilidade de cimentos-cola de presa rápida com a lâmina cerâmica. Com o objetivo de avaliar efeitos do processo de hidratação na compatibilidade de materiais e interfaces. Concluídos os primeiros ensaios laboratoriais, foram realizados ensaios ‘in situ’ com lâmina cerâmica de dimensões de 1,0x1,0m e 0,4x0,4m, variando o suporte entre betonilha e lamina cerâmica. Para concluir, realizaram-se ensaios laboratoriais para avaliar a influência da aplicação de primários de aderência, no processo de colagem de lâmina cerâmica.
In the present study, various types of adhesive mortars were characterized for the adhesion in difficult surfaces. This characterization was performed in powder, fresh and hardened state, to determine the most suitable mortar for the proposed goals. Later, thin ceramic tiles, with and without the backside grid, was also characterized. This characterization was performed taking into account the water absorption, porosity, water vapour permeability, weight loss on ignition at 500º and 900°C and evaluating the adhesion of mortar using the selection made previously. Given the differences in the obtained results of adhesion tests of the ceramic blade, with and without the backside grid, it was decided to rebuild the backside of the thin tiles. This reconstruction was carried out varying the type of grid, type of adhesive and the type of aggregates bonded in order to improve the adhesion. The adhesion was subsequently studied with these new surfaces. Although the results were not the expected ones, it was decided to assess the drying process and the effect of the comb used in the application of mortar, since this influence the amount of mortar involved in the process. The compatibility of for setting cement-based mortar with the thin tiles was also evaluated. In order to evaluate the effects of the hydration process, in the compatibility of the materials and interfaces. To complete the initial laboratory tests, trials were conducted in situ with thin tiles of dimensions 1,0x1,0m and 0,4x0,4m, using supports like floor screed and thin tiles. At last, laboratory tests were performed to evaluate the influence of application of adhesion primaries in the process of bonding thin tiles.
Description: Mestrado em Engenharia Civil
URI: http://hdl.handle.net/10773/11158
Appears in Collections:DECivil - Dissertações de mestrado
UA - Dissertações de mestrado

Files in This Item:
File Description SizeFormat 
7631.pdf4.11 MBAdobe PDFView/Open


FacebookTwitterLinkedIn
Formato BibTex MendeleyEndnote Degois 

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.