 Avaliação de ligantes minerais em argamassas-cola
Please use this identifier to cite or link to this item http://hdl.handle.net/10773/7946

title: Avaliação de ligantes minerais em argamassas-cola
authors: Linhares, Patrícia Ferreira
advisors: Ferreira, Víctor Miguel Carneiro de Sousa
keywords: Engenharia de materiais
Argamassas - Ligantes
Cimentos
Pozolanas
Metacaulino
issue date: 2011
publisher: Universidade de Aveiro
abstract: Neste trabalho, foram caracterizados os cimentos em Portugal, associados ao fabrico de argamassas, e foi comprovado que necessitam de alguma adaptabilidade. Com o objectivo de avaliar e, possivelmente, melhorar as propriedades dos cimentos-cola, foram adicionadas pozolanas artificiais (metacaulinos) como substituinte parcial e como complemento do cimento. Foram realizados ensaios físicos, mecânicos e químicos às pozolanas comprovando-se a existência de reactividade pozolânica, embora com graus distintos. Verificou-se que a aderência dos cimentos-cola é fortemente influenciada pelas condições de cura. O efeito pozolânico é evidenciado em condições de imersão em água. A aderência dos cimentos-cola, com e sem, adição de pozolanas à temperatura, ambiente apresenta comportamento semelhante. Avaliou-se a deformação transversal dos cimentos-cola, uma vez que seria expectável que a redução do cimento, através da substituição por pozolanas, originasse produtos menos rígidos e, deste modo, mais flexíveis. Os ensaios realizados permitiram concluir que a adição de pozolanas não desenvolve variações significativas na deformabilidade dos materiais, não limitando as propriedades dos cimentos-cola.

In this work, Portuguese cements used for the production of mortars were characterized and it was verified that some adjustments are needed. In order to evaluate and possibly improve the properties of cementitious adhesives, artificial pozzolans (metakaolin) were added as complement and partial substitute of cement. Physical, mechanical and chemical tests were carried out on pozzolans, proving the existence of pozzolanic reactivity, although with different degrees. It was found that in cementitious adhesives, adhesion is strongly influenced by the curing conditions. Pozzolanic effect is evident under water immersion conditions. Cementitious adhesives adherence, with and without pozzolan, showed similar behavior at room temperature. Transversal deformation was evaluated in cementitious adhesives, with pozzolan substitutions and, as it would be expected, decrease of cement fraction leads to less rigid and more flexible products. The addition of pozzolans does not develop significant changes in the deformability of the material but it doesn’t limit cementitious adhesives properties.
description: Mestrado em Engenharia de Materiais
URI: http://hdl.handle.net/10773/7946
appears in collectionsCV - Dissertações de mestrado
UA - Dissertações de mestrado

files in this item

file description sizeformat
5640.pdf2.61 MBAdobe PDFview/open
statistics

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

 

Valid XHTML 1.0! RCAAP OpenAIRE DeGóis
ria-repositorio@ua.pt - Copyright ©   Universidade de Aveiro - RIA Statistics - Powered by MIT's DSpace software, Version 1.6.2