 Caracterização física de ferrites de níquel preparadas por sol-gel
Please use this identifier to cite or link to this item http://hdl.handle.net/10773/2641

title: Caracterização física de ferrites de níquel preparadas por sol-gel
authors: Medinas, Luís Miguel Cunha
advisors: Valente, Manuel Almeida
keywords: Engenharia física
Ferrites
Propriedades magnéticas
Propriedades eléctricas
Nanopartículas
issue date: 2009
publisher: Universidade de Aveiro
abstract: Foram preparadas duas amostras de ferrites de níquel sintetizadas pelo método de sol-gel, utilizando como precursores o nitrato de níquel e nitrato de ferro numa proporção de 1:1 que posteriormente foram dissolvidos em ácido cítrico em diferentes proporções nas amostras 1 e 2 para a formação do gel. O processo de calcinação das amostras foi efectuado a 800ºC num forno tubular horizontal e num microondas doméstico durante o mesmo período de tempo. Pretendeu-se comparar os resultados das duas amostras calcinadas em ambos os dispositivos. Foram realizadas caracterizações estruturais por difracção de raios-X (DRX) onde não se obteve uma fase única de NiFe2O4 nas duas amostras. A caracterização eléctrica revelou um elevado valor da constante dieléctrica nas amostras revelando baixas perdas e comparou-se os resultados obtidos entre as amostras. No caso da caracterização magnética verificou-se que as amostras possuíam baixa magnetização comparada com o “bulk” e verificou-se que no tratamento térmico realizado no micro-ondas as amostras obtiveram valores mais elevados de magnetização de saturação e magnetização remanescente quando comparado com o tratamento térmico realizado no forno.

It was prepared two samples of nickel ferrite synthesized by the sol-gel method, using as precursors nickel nitrate and iron nitrate in a 1:1 ratio which were later dissolved in acid in different proportions in samples 1 and 2 for gel formation. The process of calcination of the samples was carried out at 800ºC in a horizontal tube furnace and a microwave oven during the same period of time. Intention was to compare the results of two samples calcined in both devices. Structural characterizations were performed by X-ray diffraction (XRD) which was not obtained a single phase of NiFe2O4 on the two samples. The electrical characterization revealed a high value of dielectric constant in samples showing low dielectric losses and compared the results between samples. In the case of magnetic characterization was found that the samples had low magnetization compared with the "bulk" and it was found that the thermal treatment in the microwave samples resulted in higher values of magnetic saturation and magnetic remanescent compared to thermal treatment in the furnace.
description: Mestrado em Engenharia Física
URI: http://hdl.handle.net/10773/2641
appears in collectionsFIS - Dissertações de mestrado
UA - Dissertações de mestrado

files in this item

file sizeformat
2010000260.pdf1.08 MBAdobe PDFview/open
statistics

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

 

Valid XHTML 1.0! RCAAP OpenAIRE DeGóis
ria-repositorio@ua.pt - Copyright ©   Universidade de Aveiro - RIA Statistics - Powered by MIT's DSpace software, Version 1.6.2